Repository logo
Institutional Repository
Communities & Collections
Browse
Quick Links
  • Central Library
  • Digital Library
  • BHU Website
  • BHU Theses @ Shodhganga
  • BHU IRINS
  • Login
  • English
  • العربية
  • বাংলা
  • Català
  • Čeština
  • Deutsch
  • Ελληνικά
  • Español
  • Suomi
  • Français
  • Gàidhlig
  • हिंदी
  • Magyar
  • Italiano
  • Қазақ
  • Latviešu
  • Nederlands
  • Polski
  • Português
  • Português do Brasil
  • Srpski (lat)
  • Српски
  • Svenska
  • Türkçe
  • Yкраї́нська
  • Tiếng Việt
Log In
New user? Click here to register.Have you forgotten your password?
  1. Home
  2. Browse by Author

Browsing by Author "R.D.K. Misra"

Filter results by typing the first few letters
Now showing 1 - 2 of 2
  • Results Per Page
  • Sort Options
  • Loading...
    Thumbnail Image
    PublicationArticle
    ELECTROCHEMICAL AND AES INVESTIGATIONS OF SOME METALLIC GLASSES IN SULPHURIC ACID SOLUTION.
    (1987) I.B. Singh; R.D.K. Misra; T.K.G. Namboodhiri; R.S. Chaudhary
    No passivation is observed for 0040 alloy whereas all the other alloys passivated in sulphuric acid solutions. Initial dissolution of the alloy in the active region is essential for passivation in molybdenum containing alloys and the concentration of Mo in the passive film is less than that of in the bulk of the alloys. Better passivation is observed in 2826 alloy when the dissolution rate is high in the active region. Prepassive film on 2826MB and 2826 alloys is nickel rich which changes to iron rich passive film at higher anodic potentials. In 2826A alloy, chromium and phosphorous concentrations are higher in the passive film.
  • Loading...
    Thumbnail Image
    PublicationConference Paper
    ELECTROCHEMICAL AND AES INVESTIGATIONS OF SOME METALLIC GLASSES IN SULPHURIC ACID SOLUTION.
    (1987) I.B. Singh; R.D.K. Misra; T.K.G. Namboodhiri; R.S. Chaudhary
    No passivation is observed for 0040 alloy whereas all the other alloys passivated in sulphuric acid solutions. Initial dissolution of the alloy in the active region is essential for passivation in molybdenum containing alloys and the concentration of Mo in the passive film is less than that of in the bulk of the alloys. Better passivation is observed in 2826 alloy when the dissolution rate is high in the active region. Prepassive film on 2826MB and 2826 alloys is nickel rich which changes to iron rich passive film at higher anodic potentials. In 2826A alloy, chromium and phosphorous concentrations are higher in the passive film.