Microwave-assisted boron and nitrogen co-doped reduced graphene oxide as a transparent conductive electrode

Abstract

A crystalline Boron (B)- and Nitrogen (N)-co-doped microwave-assisted reduced graphene oxide (BNMRGO) film was investigated as a potential transparent conducting electrode (TCE) material. X-ray diffraction results revealed the good crystallinity of the BNMRGO film, and the presence of a (0004) reflection plane indicated the formation of a few small domains of hexagonal boron nitride in the microwave assisted reduced graphene oxide (MRGO) sheets under the co-doping process. Raman and X-ray photoelectron spectroscopic results indicated a reduction of sp3 carbon centers upon co-doping. The ID/IG ratio decreased after co-doping from 0.89 to 0.24, indicating a low average defect density of ∼1.01 × 1010 cm-2. Optoelectronic characterization of the BNMRGO film on a glass substrate revealed a high optical transparency of 82% at 550 nm and a low sheet resistance (Rsh) of 355 Ω/sq, which was lower than that observed from the MRGO sheets (Rsh = 719 Ω/sq). BNMRGO provided a ratio between the direct conductivity (σdc) to the optical conductivity (σoc), that is, the figure of merit of a TCE material, of 5.96. Overall, this work paves the way toward developing a manufacturable TCE. © 2017 Author(s).