Comparative Dielectric and Ferroelectric Characteristics of Bi0.5Na0.5TiO3, CaCu3Ti4O12, and 0.5Bi0.5Na0.5TiO3–0.5CaCu3Ti4O12 Electroceramics

Abstract

Abstract: The dielectric and ferroelectric characteristics of Bi0.5Na0.5TiO3 (BNT), CaCu3Ti4O12 (CCTO), and 0.5Bi0.5Na0.5TiO3–0.5CaCu3Ti4O12 (BNT/CCTO) ceramics are compared. X-ray diffraction patterns confirmed the formation of single phase of all the ceramics after sintering at 950°C for 15 h. Scanning electron microscopy images of the sintered ceramics reveal average grain sizes in the range from 200 nm to 2.5 μm. Energy-dispersive x-ray mapping and x-ray photoelectron spectroscopy show the presence of the elements Bi, Na, Ca, Cu, Ti, and O with uniform distribution in the ceramics. BNT/CCTO exhibits high dielectric constant (εr ∼ 6.9 × 104) compared with BNT (εr ∼ 0.13 × 104) and CCTO (εr ∼ 1.68 × 104) ceramics at 1 kHz and 503 K. The high dielectric constant of BNT/CCTO compared with BNT and CCTO is associated with a major contribution from grain boundaries, as confirmed by impedance and modulus analyses. The P–E hysteresis loop of all the ceramics measured at room temperature and 50°C exhibited typical ferroelectric nature. The remanent polarization (Pr) of BNT (1.58 μC/cm2) and CCTO (0.654 μC/cm2) ceramics are higher than that of BNT/CCTO (0.267 μC/cm2) ceramic. Graphical Abstract: [Figure not available: see fulltext.] © 2016, The Minerals, Metals & Materials Society.